ZH5005/ZH1032

牌号（Shop sign）:ZG-P-5005/ZG-I-1032 1.特性：中高硬度，中高密度 Characteristics:Medium to high hardness，medium to high density PU resin for shoe sole. 2.用途：适用于连帮鞋、沙滩鞋鞋底的生产 Application：Applicable for the production of shoe sole with the upper and slippers for men and women. 3. 原液特性Typical properties of PU Resin 品 名 Name of products 外 观 Appearance 粘 度 Viscosity （Pa·s/50℃） 密 度 Density （g/cm3/40℃） 包 装 Package （kg） ZG-P-5005 白色或淡黄，液状无异物 White or pale yellow, liquid, no foreign material 0.50-0.80 1.16-1.20 18 ZG-I-1032 透明液体无异物 Transparent liquid, no foreign material 0.10-0.30 1.18-1.20 20 参考发货配比(Reference shipments ratio)：A/B=30/25(桶) Reference shipments ratio: A/B=30/25(barrel) 4. 催化剂与辅助剂Catalysts and auxiliary agents： ZG-P-5005/ZG-AC-2/水 =18kg/200-300g/30-60g 注：辅助剂的加入在不同地区和不同环境及不同生产条件作相应调整。 ZG-P-5005/ZG-AC-2/water =18kg/200-300g/30-60g Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions. 5. 成型条件及物性值(Molding conditions & physical properties)： 反应性 Reactivity 技术指标 Technical index 测试项目 Test item 参考物性值 Reference physical properties 参考配比 Reference ratio P+C/I 100/79-83 鞋底成型密度 Molded density of sole （g/cm3） 0.38-0.55 使用温度 Using temperature（℃） A料:45-50;B料:38-42 A material: 45-50; B material:38-42 硬度(A型) Hardness (type A) 50-70 乳白时间 Cream time（s） 5-9 拉伸强度 Tensile strength（MPa） 6.0-8.0 升起时间 Rise time（s） 30-45 伸长率 Elongation（％） 350-450 金属模具温度 Metal mold temperature （℃） 45-55 DIN耐磨 DIN abrasion resistance（mm3） ≦400 脱模时间 Demould time （min） 2.5-4 自由泡密度 Free foam density （g/cm3） 0.24-0.30 耐折性(常温） (4万次裂口长度，mm) Folding endurance (room temperature) (40,000 gap length mm) ＜8