ZH-8850/ZH-7620

1.特性：中低硬度，低密度 Characteristics:Medium to low hardness，low density PU resin for shoe sole. 2.用途：适用于吸膜料的生产 Application：Applicable for the production of suction film shoe sole for men and women. 3. 原液特性Typical properties of PU Resin 品 名 Name of products 外 观 Appearance 粘 度 Viscosity （Pa·s/50℃） 密 度 Density （g/cm3/40℃） 包 装 Package （kg） ZG-P-8850 白色或淡黄，液状无异物 White or pale yellow, liquid, no foreign material 0.60-1.00 1.16-1.20 18 ZG-I-7620 透明液体无异物 Transparent liquid, no foreign material 0.10-0.30 1.18-1.20 20 参考发货配比(Reference shipments ratio)：A/B=30/25(桶) Reference shipments ratio: A/B=30/25(barrel) 4. 催化剂与辅助剂Catalysts and auxiliary agents： ZG-P-8850/ZG-AC-2/水 =18kg/220-280g/60-100g 注：辅助剂的加入在不同地区和不同环境及不同生产条件作相应调整。 ZG-P-8850/ZG-AC-2/water =18kg/220-280g/60-100g Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions. 5. 成型条件及物性值(Molding conditions & physical properties)： 反应性 Reactivity 技术指标 Technical index 测试项目 Test item 参考物性值 Reference physical properties 参考配比 Reference ratio P+C/I 100/64-68 鞋底成型密度 Molded density of sole （g/cm3） 0.35-0.40 使用温度 Using temperature（℃） A料:45-50;B料:38-42 A material: 45-50; B material:38-42 硬度(A型) Hardness (type A) 25-35 乳白时间 Cream time（s） 5-9 拉伸强度 Tensile strength（MPa） 6.0-8.0 升起时间 Rise time（s） 30-45 伸长率 Elongation（％） 350-450 金属模具温度 Metal mold temperature （℃） 45-55 DIN耐磨 DIN abrasion resistance（mm3） ≦500 脱模时间 Demould time （min） 5-8 自由泡密度 Free foam density （g/cm3） 0.18-0.22 耐折性(常温） (4万次裂口长度，mm) Folding endurance (room temperature) (40,000 gap length mm) ＜8